Storage tanks corrosion protection

1. Corrosion

Corrosion is a naturally occurring effect, defined as destruction of substance, usually metals, or alteration of their properties due to the environment impact. As well as other natural events, such as natural disasters, corrosion may bring about dangerous and finance-consuming damage.

Corrosion is the process of metal destruction in the course of its physical-chemical or chemical interaction with the external environment. Corrosion is usually divided into:

  • chemical – occurring without electric current;
  • electrochemical – accompanied by electric current (corrosion current);
  • mechanic-chemical (corrosion-mechanic wear-out), which implies that the first two types of process act together with mechanic impact: friction, cyclic bending load, vibration, etc.)

In the course of operation tanks are subject to corrosion both from the outside and the inside.

The external side of the tank stains under the influence of atmospheric moisture and corrosive elements (particles) in the air.

The inside corrosion depends basically on the frequency of the tank’s loading with oil products, on chemical composition of the products, on the presence of water in the fuel. The tempo and the characteristics of the corrosion process are the most evident on the inside surface of the tanks at the points of separation of two structures: oil product – bottom water, oil-product – gas-vapour mixture.

Humidity and the external atmosphere temperature, as well as corrosion resistance of steel, — all influence the intensity of corrosion.

2. Industrial Painting of the Tank's Outside Surface

According to the rules of installation of vertical cylindrical steel tanks for oil and oil products the surface of the metal frameworks exposed to open air should be painted with lacquer paint materials. While choosing the colour of the corrosion protection coating for steel the light reflection factor should be considered.

The state of corrosion protection coating of the outside surface of the above ground tanks should be controlled periodically. Control is meant for checking defects in the external layer of the protective coating, continuity of the coating throughout the external surface, the rate of adhesion of the coating to the metal surface of the tank.

2.1. Preparation of the external surface of a vertical tank for applying corrosion protection coating for steel:

While preparing the external surface for the industrial painting services the worn out layer of the old protective coat, corrosion traces and dirt are removed either manually or by mechanical method.

Stain is removed either by cleaning pads № 25, 16 and 12 or wire brushes, or by chemical method, using cleaner, containing 35 % of orthophosphoric acid, 20 % of ethylic alcohol, 5 % of butyl alcohol, 1 % of hydroquinone and 39 % of water.

The cleaner is applied on the stained surface for 3-5 min, after which it is washed with hot water together with the corrosion products. After this the surface is wiped.

Mechanical cleaning and degreasing is done for the whole outside surface of the tank.

The prepared surface should be thoroughly wiped and dried.

2.2. Technological process of applying the industrial coating:

A priming industrial coating is applied on the prepared tank surface with a pneumatic spray gun. It is highly important to avoid paint drips. This process is meant for protecting metal from corrosion and ensuring adherence of the paint coating with the metal.

After the work is finished, the paint corrosion protection coating of light colour is applied on the outside surface. It gives heat-reflecting effect and corrosion preventive characteristics.

The finished painted surface should have equal layer thickness without paint dips and other defects.

2.3. Soil corrosion protection of the tank bottom:

The problem of tank bottom corrosion is very serious. For example, penetrating corrosion bottom destruction of the tanks, used for oil settling, and flow lines may lead to oil spills that pollute the environment. Moreover, there appears the need to replace the tank bottoms already after 5-6 years of operation, which is complicated, considering the diameter of the bottom equal to almost 50 m (for vertical steel tank 20 000).

The soil corrosion may be avoided by arranging water-proof layer and by using electro-chemical protection, when galvanic protectors are connected to the tank bottom. Apart from this, the bottom may be effectively protected by means of cathodic protection.

When the corrosion protection companies work with the outside surface of the tank bottom they should meet the following requirements:

  • Arranging the foundation and the basement of the tank should provide drainage of ground water and precipitation from the bottom;
  • It is not necessary to apply protective coating on the outside surface of the tank when a hydrophobic sand-bitumen layer is arranged (at the rate of 1:9 in the mass density). The applied sand and bitumen should not contain corrosion-active elements.

It is important to consider environmental protection regulations, requirements of accident prevention and safety instructions and other standards, controlling performing of this type of work.

2.4. Electro-chemical corrosion protection:

Electro-chemical storage tank corrosion protectionis based on the ability of metals to stop staining under the influence of flow of direct current.

The surface of any metal is inhomogeneous as regards galvanic characteristics, and this is to be seen as the main reason for metal to suffer corrosion in electrolytic conductors’ solutions, among which are sea water, local water and bottom water. In this case only areas with the most negative potential (anodes) are destroyed. While the areas of surface with the more positive potential (cathodes) do not show destruction.

The scheme of effect of the electrochemical protection implies that the whole surface of the metal framework is turned into one big indestructible cathode. Anodes are represented by electrodes of more electronegative material, connected to the bottom of the protected construction. They are called galvanic protectors.

The protective current appears as a result of operation of the galvanic pair: galvanic protector – protected construction. Protectors tend to gradually wear out, giving protection to the parent metal, that is why they are often called “sacrificial anode”.

Electro-chemical storage tank corrosion protection is the only effective method against the most local types of metal corrosion (pitting and gap corrosion, contact corrosion, intergranular corrosion and cracking). At the same time it helps to prevent from the further development of the on-going corrosion process, thus it is equally effective as for tanks and equipment under construction and for those, already in operation, too.

Galvanic protectors’ method is usually applied in combination with paint and lacquer coatings. Such combination of passive protection (painting) with active protection (electrochemical) enables to reduce the expenditure of galvanic protectors and prolong their operating life, to ensure more even distribution of electric protective current over the surface of protected constructions. It also helps to balance the coating defects, arising from its damage in the course of assembly, transporting and operation, including the results of natural ageing (swelling, buckling, cracking, flacking).

Protective current goes exactly to those metal areas, where the density of the coating is damaged. It reaches all shadowed areas, gaps, hollow spaces, preventing the bare metal from staining. It should be noted that in the course of cathodic polarization local and bottom water shows certain salt gel that contains insoluble Ca and Mg salts and plays the role of additional coating.

Along with this, electrochemical protection can provide full safety from corrosion without painting too. In this case the higher protective current density should be provided for unpainted steel surface, which will demand increasing the number of galvanic protectors and will enforce their expenditure. However, if we take into consideration the labour intensity of applying the protective coating, especially for tanks in operation, this method of corrosion preventive protection seems to be potentially productive.

As most metal frameworks are produced of steel, galvanic protectors may be made of metals with more negative electric potential, compared to steel. The basic are zinc, aluminum, magnesium.

It should be taken into consideration that if the potential shift to negative direction exceeds a certain limit, there is a threat of so-called “over-protection”, connected with release of hydrogen, changes of near-electrode layer’s composition, and other effects, that may lead to corrosion boosting.

3. Industrial Painting of the Internal Tank Surface

Industrial coating services for internal surface are very labour-intensive. This is connected with complicated procedures of surface preparation and applying corrosion protection coating for steel.

3.1. Metal processing before painting:

The technological process of tank’s inside surface preparation differs much from the one for the external surface. We can divide it into several stages:

  1. Oil products’ discharge;
  2. Internal surface cutting down (stripping);
  3. Tank degassing;
  4. Degreasing of the inside surface;
  5. Sand-blasting;
  6. Cleaning the inside surface from sand and dirt;
  7. Applying the cleaner to the corrosion areas;
  8. Washing the internal surface with hot water;
  9. Drying from the inside at 5-20 °С for 2-3 days (manway plates and gate valves kept open);
  10. Checking the quality of preparation work and suitability for applying protective coating.

3.2. Technological process of applying the corrosion protection coating:

A priming coat is applied on the prepared inside tank surface with a pneumatic spray gun. It is highly important to avoid paint drips. This process is meant for ensuring adherence of the paint coating with the metal.

The inside surface of underground and above ground tanks are covered with paint and lacquer materials in 2-4 layers with the successive drying of each layer separately.

After the work is finished acceptance certificate is signed, which has to be accompanied by certificates for materials used.

Table: «The level of aggressive impact of the external environment on the steel structures inside a vertical steel tank »:
Elements of a tank:
Level of product’s aggressive impact on the steel elements of a vertical tank:
Clean oil
Masut, diesel fuel, kerosene
petrol
internal surface of the bottom and the lower ring at 1 m’ height from the bottom
medium rings, lower parts of the pontoons and floating roofs
upper ring (splash zone)
tank roof, top and edges of the pontoons and floating roofs
Note: The rate of aggressive impact of masut is considered at the temperature level, not exceeding 90°C.

4. Methods of Storage Tank's Corrosion Protection

4.1. Approach to vertical tanks’ industrial painting:

To reduce the danger of corrosion damage to the metal frameworks, that can bring the tank out of operation, it is essential to provide a certain system of rust and corrosion protection measures, that includes applying protective coat and (or) increasing the thickness of the metal plates (corrosion allowance), which is meant to consider the possible loss of the details’ thickness as a result of corrosion.

Moreover, you should provide periodic examination of the full surface of the tank not less than once in every 5 years for revealing corrosion damage and the areas of surface with damaged pain coating. If necessary, the protective coat is restored.

If the metal frameworks of tank roof and upper rings of the shell show extremely high tempo of corrosion process it is possible to use inert-gas atmosphere as additional method of corrosion protection.

4.2. Considering the level of aggressive impact of the stored product and atmosphere:

When choosing the rust and corrosion protection method and determining the corrosion allowances one should consider the level of aggressive impact of the environment on the metal details inside the tank and on its outside surface, exposed to the open air. The level of aggressive impact of the stored product on the inside structural elements is shown in the Table below.

The level of influence of external atmosphere on the open-air elements is determined by the temperature and humidity parameters of the air and loading of corrosion active gas in the air in accordance with the construction standards and regulations.

Structural elements of the tank: the extent of the aggressive impact of the stored products:
  crude oil black oil, diesel fuel, kerosene gasoline
the internal surface of the bottom and the lower belt of the shell on height of 1m from the bottom aggressive medium aggressive medium weakly aggressive
the middle belt of the shell, the lower parts of the pontoons and floating roofs weakly aggressive weakly aggressive weakly aggressive
the upper zone of the shell (zone of periodic moistening) aggressive medium weakly aggressive aggressive medium
roof, top and side surfaces of pontoons and floating roofs aggressive medium aggressive medium weakly aggressive

Provided the level of hydrogen disulfide in the crude oil is higher than 10 g/l or it contains hydrogen disulfide and carbon dioxide in any proportion, the rate of aggressive impact on the internal surface of the bottom, the lower ring, roof, top and edges of the pontoons and floating roofs increases by one level.

Keeping the thickness of metal structures exposed to mildly aggressive influence is achieved only by means of corrosion allowances.

If the frameworks are subject to moderately aggressive and highly corrosive impact, the safe operation of the tank is ensured, apart from corrosion allowances, by industrial painting services.

This method helps to raise the reliability of the metal frameworks in case of local destruction of protective coat before the planed examining of the corrosion condition of the tank.

The rate of corrosion allowance is set based on the tempo of corrosion damage process, which is determined by the type of environment aggressiveness:

  • Mildly aggressive: rate of deterioration not more than 0,05 mm per year;
  • Moderately aggressive: rate of deterioration from 0,05 to 0,5 mm per year;
  • Highly-corrosive: rate of deterioration more than 0,5 mm per year.

Electrochemical corrosion protection of the structural elements of the tank is carried out by ground and cathodic protection units. The method is chosen based on the technical-economic parameters.

4.3. Requirements for surface preparation before industrial painting services:

Surfaces of the metal structures, prepared for rust and corrosion protection, should not have:

  • Slug residues, weld spatter, cold laps, welding joints’ irregularities;
  • Cutting off and gas cutting traces;
  • Sharp edges to radius less than 3.0 m on the inside and 1.5 m on the outside surface of the tank body and the floating roof;
  • Auxiliary elements, used in the course of assembly, installation, transportation, lift-up works, and the traces of their welding;
  • Chemical contamination (flux residues, substances used for defect detection of the welding joints) that are located on the seams’ surface and near them;
  • Oil (greasy), mechanical and other contamination.

The welding joints should have smooth connection with the base metal without cutoffs and cold laps.

All internal elements of the tank, welded to the shell, bottom or roof, have to be scalded along the edges to avoid appearance of hollow spaces and spacing gaps.

Apart from this, all elements exposed to open air under the influence of moderately aggressive environment, should also be scalded along the edges to avoid appearance of hollow spaces and spacing gaps.

Before the corrosion protection coating for steel is applied all surfaces must be degreased to the 2nddegree, cleaned from oxides to the 1st degree for applying sprayed metal and paint coating or to the 1st-2nd degree for applying paint coating. Dust should be alsoremoved from the surface.

4.4. Choosing the type of corrosion preventive coating:

Metallized paint coating is used for corrosion protection of metal elements inside a tank. For elements of metal structures in the open air paint coating should be used.

The operating period of effectiveness for protective coating should be not less than 10 years.